Assessment of Corrosion in Offshore R.C. Piers and Use of Microsilica to Reduce Corrosion Induced Oxidation (A Case Study of Wharves 11 and 12 in Imam Khomeini Port, Iran) | ||
| Civil Engineering Infrastructures Journal | ||
| دوره 55، شماره 2، اسفند 2022، صفحه 333-350 اصل مقاله (802.96 K) | ||
| نوع مقاله: Research Papers | ||
| شناسه دیجیتال (DOI): 10.22059/ceij.2021.325670.1761 | ||
| نویسندگان | ||
| Abdolreza Tangtakabi1؛ Mohammad Hassan Ramesht* 2؛ Ali Golsoorat pahlaviani2؛ Tovhid Pourrostam2 | ||
| 1Ph.D. Candidate, Department of Civil Engineering, Islamic Azad University, Central Tehran Branch, Tehran, Iran. | ||
| 2Assistant Professor, Department of Civil Engineering, Islamic Azad University, Central Tehran Branch, Tehran, Iran. | ||
| چکیده | ||
| Deterioration due to corrosion is an important issue affecting the durability, strength, and sustainability of buildings and structures. Many cities are located in coastal areas and many reinforced concrete structures in these areas are exposed to chloride aggressive marine environments. Therefore, it is important to provide protection and offer appropriate repair methods of buildings vulnerable to the degrading effects of corrosion. The present study sets out to identify and evaluate the causes and extent of corrosion observed in Piers 11 and 12 in Imam Khomeini port, Iran. The microsilica is used to reduce corrosion. In order to achieve the above-mentioned goals, a number of experimental field tests were performed to determine the level of concrete condition in terms of reinforcement corrosion. Some tests were conducted to determine the conditions of concrete piers in terms of reinforcement corrosion. Then a reinforcement corrosion current density test is performed using a potentiostat involving a placement process; with different water-to-cement ratios and superplasticizers, the microsilica content was 5%, 10%, and 15%. Microsilica can serve as an alternative to cement and was measured according to the ASTM standards. Microsilica was exposed to aggressive conditions at different periods and a concrete compressive strength test was performed. The results showed that the compressive strength and corrosion resistance of the concrete increased for concrete mixture containing 10% microsilica with a water-to-cement ratio of 34% and a superplasticizer ratio of 6%. | ||
| کلیدواژهها | ||
| Density؛ Imam Khomeini Port؛ Microsilica؛ Offshore Structures؛ Reinforcement Corrosion؛ Wharf | ||
| مراجع | ||
|
Abedini, M. and Zhang, C. (2021). "Dynamic vulnerability assessment and damage prediction of RC columns subjected to severe impulsive loading", Structural Engineering and Mechanics, 77(4), 441.
ACI 201. (2008). Guide to durable concrete, American Concrete Institute.
ACI 222 Standard. (2001). Protection of metals in concrete against corrosion, American Concrete Institute.
Antunes, D., Martins, R., Carmo, R., Costa, H. and Júlio, E. (2021). "A solution with low-cement light weight concrete and high durability for applications in prefabrication", Construction and Building Materials, 275, 122153.
ASTM C597. (2002). Standard test method for pulse velocity through concrete, ASTM International.
ASTM C114. (2017). Chemical Analysis of Hydraulic Cement, ASTM International.
ASTM. (2021). Standard specification for concrete aggregates, Annual Book of ASTM Standards, 04.02, USA.
Babaee, M. and Castel, A. (2016). "Chloride-induced corrosion of reinforcement in low-calcium fly ash-based geopolymer concrete", Cement and Concrete Research, 88, 96-107.
Babaee, M. and Castel, A. (2018). "Chloride diffusivity, chloride threshold, and corrosion initiation in reinforced alkali-activated mortars: Role of calcium, alkali, and silicate content", Cement and Concrete Research, 111, 56-71.
Bagheri, A., Zanganeh, H., Alizadeh, H., Shakerinia, M. and Marian, M.A.S. (2013). "Comparing the performance of fine fly ash and silica fume in enhancing the properties of concretes containing fly ash", Construction and Building Materials, 47, 1402-1408.
Baqheri, A.R., Zanganeh, H., Samadzad, H. and Kiani, A.L.A.H. (2012). "Assessing the durability of binary and ternary concretes using rapid chloride resistance test and the accelerarted rebar corrosion test", The International Congress on Durability of Concrete, Tehran, Iran.
Ganjian, E. and Pouya, H.S. (2009). "The effect of Persian Gulf tidal zone exposure on durability of mixes containing silica fume and blast furnace slag", Construction and Building Materials, 23(2), 644-652.
Gu, P., Beaudoin, J., Zhang, M.H. and Malhotra, V. (2000). "Performance of reinforcing steel in concrete containing silica fume and blast-furnace slag ponded with sodium-chloride solution", Materials Journal, 97(3), 254-262.
He, B., Gao, Y., Qu, L., Duan, K., Zhou, W. and Pei, G. (2019)."Characteristics analysis of self-luminescent cement-based composite materials with self-cleaning effect", Journal of Cleaner Production, 225, 1169-1183.
He, X., Zheng, Z., Yang, J., Su, Y., Wang, T. and Strnadel, B. (2020). "Feasibility of incorporating autoclaved aerated concrete waste for cement replacement in sustainable building materials", Journal of Cleaner Production, 250, 119455.
Liu, J., Huang, H., Ma, Z.J. and Chen, J. (2021). "Effect of shear reinforcement corrosion on interface shear transfer between concretes cast at different times", Engineering Structures, 232, 111872.
Li, C.Q. and Zheng, J.J. (2005). "Propagation of reinforcement corrosion in concrete and its effects on structural deterioration", Magazine of Concrete Research, 57(5), 261-271.
Parrott, L. (1994). "A study of carbonation-induced corrosion", Magazine of Concrete Research, 46(166), 23-28.
Moffatt, E. and Thomas, M. (2018). "Performance of 25-year-old silica fume and fly ash lightweight concrete blocks in a harsh marine environment", Cement and Concrete Research, 113, 65-73.
Maierhofer, C., Reinhardt, H.W. and Dobmann, G. (2010). Non-destructive evaluation of reinforced concrete structures: Non-destructive testing methods, Woodhead Publishing.
Poston, R.W., Kesner, K., McDonald, J.E., Vaysburd, A.M. and Emmons, P.H. (2001). "Concrete repair material performance, Laboratory study", Materials Journal, 98(2), 137-147.
Pandey, A. and Kumar, B. (2019). "Evaluation of water absorption and chloride ion penetration of rice straw ash and microsilica admixed pavement quality concrete", Heliyon, 5(8), e02258.
Roy, S., Poh, K. and Northwood, D. (1999). "Durability of concrete accelerated carbonation and weathering studies", Building and Environment, 34 (5), 597-606.
Ryan, E.W. (2011). “Comparison of two methods for the assessment of chloride ion penetration in concrete: A field study”, M.Sc. Thesis, University of Tennessee.
Siddique, R. (2011). "Utilization of silica fume in concrete: Review of hardened properties", Resources, Conservation and Recycling, 55(11), 923-932. Tajdini, M., Bargi, M.M. and Rasouli Ghahroudi, O. (2021). “An investigation on the effects of adding nano-sio2 particles and silica Ffume with different specific surface areas on the physical and mechanical parameters of soil-cement materials”, Civil Engineering Infrastructures Journal, 54(1), 93-109.
Zhang, C., Abedini, M. and Mehrmashhadi, J. (2020). "Development of pressure-impulse models and residual capacity assessment of RC columns using high fidelity Arbitrary Lagrangian-Eulerian simulation", Engineering Structures, 224, 111219.
Zhang, C. and Abedini, M. (2021), "Time-history blast response and failure mechanism of RC columns using Lagrangian formulation", Structures, Elsevier, 34, 3087-3098. | ||
|
آمار تعداد مشاهده مقاله: 508 تعداد دریافت فایل اصل مقاله: 949 |
||