سامانه پشتیبانی خدمات اطلاعات

  اخبار و اعلانات

 آمار

تعداد نشریات161
تعداد شماره‌ها6,532
تعداد مقالات70,501
تعداد مشاهده مقاله124,113,252
تعداد دریافت فایل اصل مقاله97,217,074
Mohamed Jaffer Sadiq, M., Samson Nesaraj, A.. (1393). Development of NiO-Co3O4 nano-ceramic composite materials as novel photocatalysts to degrade organic contaminants present in water. , 8(4), 1171-1184. doi: 10.22059/ijer.2014.810
M. Mohamed Jaffer Sadiq; A. Samson Nesaraj. "Development of NiO-Co3O4 nano-ceramic composite materials as novel photocatalysts to degrade organic contaminants present in water". , 8, 4, 1393, 1171-1184. doi: 10.22059/ijer.2014.810
Mohamed Jaffer Sadiq, M., Samson Nesaraj, A.. (1393). 'Development of NiO-Co3O4 nano-ceramic composite materials as novel photocatalysts to degrade organic contaminants present in water', , 8(4), pp. 1171-1184. doi: 10.22059/ijer.2014.810
Mohamed Jaffer Sadiq, M., Samson Nesaraj, A.. Development of NiO-Co3O4 nano-ceramic composite materials as novel photocatalysts to degrade organic contaminants present in water. , 1393; 8(4): 1171-1184. doi: 10.22059/ijer.2014.810

Development of NiO-Co3O4 nano-ceramic composite materials as novel photocatalysts to degrade organic contaminants present in water

International Journal of Environmental Research
مقاله 32، دوره 8، شماره 4، دی 2014، صفحه 1171-1184    اصل مقاله (550.52 K)
نوع مقاله: Original Research Paper
شناسه دیجیتال (DOI): 10.22059/ijer.2014.810
نویسندگان
M. Mohamed Jaffer Sadiq1؛ A. Samson Nesaraj* 2
1Department of Nanosciences and Technology, Karunya University, Coimbatore - 641 114, India
2Department of Chemistry, Karunya University,Coimbatore – 641 114, India
چکیده
Novel ceramic oxides have been increasingly focused in recent years because of their potential
applications in environmental purification especially to treat organic contaminants present in water. In this
research work, a set of NiO-Co3O4 nano-ceramic composite materials were prepared by a simple reflux
condensation method using nickel acetate / cobalt acetate as precursor salts, sodium monododecyl sulphate
(SDS) as a surfactant and N,N-Dimethylformamide (DMF) as solvent. The prepared nano-ceramic composites
were calcined at different temperatures such as 200, 400, 600 and 800oC for 2 hours each to get the phase pure
product. XRD results revealed that all the samples indexed to a cubic crystalline geometry. The presence of
metal-oxygen bond (Ni-O and Co-O) was confirmed by FTIR spectroscopy. The presence of Ni, Co and O in
the sample was confirmed by EDAX analysis. The existence of particles in nanometer range was shown by
SEM. The particle size analysis by light scattering method also confirmed the particles in nanometer range
(approximately 270 nm) in all the three samples. The optical behavior of the materials was studied by UV-Vis
and PL spectrophotometer. Photocatalytic activity studies carried out with NiO-Co3O4 (1.0:1.0) nano-ceramic
composites in presence of organic dyes such as, rhodamine B and methyl orange dyes under UV light
irradiation (for two hours) resulted in the degradation of 77% and 84% respectively.
کلیدواژه‌ها
NiO-Co3O4 nano-ceramic؛ Reflux؛ photocatalytic؛ degradation؛ Organic؛ Dyes؛ water